8620H / 21NiCrMo2 220H Hot Rolled Steel Bar For Bearings Round Shape

Categories Hot Rolled Steel Bar
Brand Name: Unite Steel
Model Number: Dia : 10-320mm
Certification: ISO/MTC/BV/SGS
Place of Origin: China
MOQ: MOQ:2-3 Ton
Price: USD 700-950 Ton
Payment Terms: D/A, L/C, D/A, D/P, T/T
Supply Ability: 3000 Ton per Month
Delivery Time: Within 15-35 days
Packaging Details: Standard seaworthy packing or as your request .
Product name: 8620H/21NiCrMo2/DIN1.6523/805 M20/EN362/SNCM 220H Hot Rolled Steel Bar ,With Black/peeled surface
Material grade: 8620H/21NiCrMo2/DIN1.6523/805 M20/EN362/SNCM 220H
Deliervy condition: annealed/hot rolled/cold drawn/quenched & tempered
Surface: black/machined/peeled/polished/turned
Certificate: ISO/MTC/BV/SGS
Process: LD+LF+VOD+CC+HOT ROLLED+CUT+SLOW COOLING+STRAIGHTENED
UT: 100% Ultrasonic according to the test standards:SEP1921-84
Shape: Round shape
  • Product Details
  • Company Profile

8620H / 21NiCrMo2 220H Hot Rolled Steel Bar For Bearings Round Shape

8620H/21NiCrMo2/DIN1.6523/805 M20/EN362/SNCM 220H Hot Rolled Steel Bar ,With Black/peeled surface


Description:

8620 is a low nickel - chromium - molybdenum medium hardenability, case hardening (carburizing) steel, generally supplied in the as rolled condition with a maximum brinell hardness of 280 (Rc30).
Characterised by good core strength and toughness in small to medium sections with case hardness up to Rc62 when carburized, hardened and tempered.
8620 can also be used (uncarburised) as a high tensile steel, which when suitably hardened and tempered can be utilized for various applications requiring good tensile strength and reasonable toughness.
Pre hardened and tempered (uncarburized) 8620 can be further surface hardened by nitriding but will not respond satisfactorily to flame or induction hardening due to its low carbon content.
8620 (carburized) is used extensively by all industry sectors for light to medium stressed components and shafts requiring high surface wear resistance with reasonable core strength and impact properties.


APPLICATIONS:

AISI 8620 is a common, carburizing alloy steel used for a variety of medium-strength applications including gears, camshafts, fasteners, and chains/chain pins. Flexibility in hardening treatments allow optimization of case/core properties. Typical uses are: Arbors, Bearings, Bushings, Cam Shafts, Differential Pinions, Guide Pins, King Pins, Pistons Pins, Splined Shafts, Ratchets, Sleeves etc..


Chemical Composition(%):

CSiMnP(max)S(max)NiCrMo
0.17-0.230.10-0.400.60-0.950.040.040.35-0.750.35-0.750.15-0.25

rocess: EAF+LF+VOD+Rolled+Heat Treatment(optional)


SIZE RANGE:

Round:

Hot Rolled:10-200mm


SURFACE FINISHES:

Black, Peeled (K12), Cold Drawn, Turned & Polished (H10, H11), Precision Ground (H9, H8)


Test: Ultrasonic test according to SEP 1921-84 .


Forging
Heat to 1150 oC and hold until temperature is uniform throughout the section. Soaking time at forging temperature should be as short as possible to avoid heavy scaling and excessive grain growth. This will vary depending on furnace conditions but 15 minutes per 25 mm of section may be used as a guide.Do not forge below 850 oC.
Following completion of forging operation, work piece should be cooled as slowly as possible in sand or dry lime etc.
Note: Case hardening steels due to their low carbon content are less susceptible to cracking than medium or high carbon steels, and may therefore be heated and cooled more rapidly.


Machining
8620 in the as rolled as supplied condition, has very good machinability and all operations such as turning, drilling, milling and tapping etc. can be carried out satisfactorily as per machine manufacturers recommendations for suitable tool type - feeds and speeds.

Welding
8620 is readily weldable in the as rolled as supplied condition. Following welding, the work piece immediately upon cooling to hand warm should be stress relieved at 630 oC - 650 oC if possible.
N.B. Welding in the carburized and heat treated condition is not recommended.
Welding Procedure
Welding of 8620 should always be carried out using low hydrogen electrodes - please consult your welding consumables supplier.



Quality 8620H / 21NiCrMo2 220H Hot Rolled Steel Bar For Bearings Round Shape for sale
Send your message to this supplier
 
From:
Enter your email please.
To: SHANGHAI UNITE STEEL TRADING CO., LTD
Subject:
Message:
Characters Remaining: (0/3000)
 
Inquiry Cart 0